The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

The application range of positive and negative twisting barbed rope is also very wide, is a good choice for purchasing barbed rope, then positive and negative twisting barbed rope compared with other barbed rope advantages? The following Haorong barbed rope factory for you to introduce the positive and negative twisting of the three advantages of barbed rope

Removal of surface-active substances by activated carbon matting. Or make the bubble unstable according to overworry, these are all reasonable countermeasures; Other strategies should also be used to minimize the amount of surfactant taken in. The introduction of organic matter can make the electroplating process speed drop sharply. Galvanized iron wire blackening can be effectively prevented, such as: the work site to keep dry, reduce and do not use chemicals, operators with clean gloves and so on. In addition, hot dipping zinc factory can be required, after dipping zinc must be passivation treatment, passivation treatment of zinc has a better anti-discoloration effect, can effectively prolong the discoloration time, the combination of the two, discoloration should be able to solve.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.