Poor pretreatment before electroplating; Bath temperature is too low; Poor quality additives or excessive additives and organic impurities can cause poor bonding. The quality of the additive also has an effect on coating foaming. Some additives react incompletely during synthesis and continue to polymerize during long-term storage or use. The additive tends to distort the lattice and create stress, causing the coating to blister.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.

Galvanized iron wire is a substance we often see in life. It is the zinc gradually plated on the metal surface through the unidirectional current in the electroplating tank. The production speed is slow, the coating is uniform, the thickness is thin, usually only 3-15 microns, the appearance is bright, the corrosion resistance is poor, and the corrosion will rust in a few months. Galvanized wire has the characteristics of thick galvanized layer, strong corrosion resistance, strong galvanized layer, etc., the products are widely used in construction, highway walls, Zahua, weaving nets.

Galvanized wire mesh is divided into hot dip galvanized wire mesh and cold galvanized wire mesh. Galvanized steel wire net selects the high quality low carbon steel wire, iron wire factory made by precision of automation machinery welding technology processing, smooth surface, firm structure, integrity is strong, even if the local cutting of galvanized steel wire net, or local also under pressure from loose phenomenon, after molding, wire mesh galvanized corrosion resistance good, has the advantage that the general steel mesh does not have.

We must have a certain understanding of the hexagonal network, we are the beautiful shape of the hexagonal network, more than the appearance of the hexagonal network is very beautiful, in fact, the practical value of survival is very high. To introduce the relevant information should be very clearly know the highway guardrail net, hexagonal wire netting in all kinds of fence netting, in the value of the high-speed on the road more MaoJian, it not only be used in all kinds of road, in a sports ball games venue and try our best to take care of landslides, also has reached very matter effectiveness.

Now many hardware manufacturers produce iron wire, and iron wire is very easy to rust, if you need to use in outdoor or humid places, generally customers will require the use of galvanized iron wire equipment to give the wire a layer of zinc, the thickness can be determined according to user requirements. Galvanized iron wire equipment is specially used for the plating of iron. Generally speaking, the stability of zinc is much higher than that of iron, and it will not rust in the daily water vapor or damp place.

2. Adjust the drawing process parameters of the water tank

Hot wire plating adopts zinc-free slag to add hot molten zinc and galvanizing, which avoids the traditional heating process, radiates 1653 hot molten zinc on surface 4102 of zinc liquid surface, and reduces the high temperature oxidation of zinc liquid surface. At the same time, the heating body is in contact with the zinc liquid, and the heat is directly transferred to the zinc liquid. The utilization rate of heat energy can reach more than 90%, and the heat radiation on the zinc liquid surface is reduced.