Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, ocean exploration, metal structure, electric power transmission, shipbuilding and other industries.

The production of large rolls of galvanized wire iron can be divided into two categories, is directly from the iron ore after iron stroke exercise out of the metal, the composition of the ore is iron oxide, silica and other miscellaneous stone.

Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is to use the lead screw above the zinc pot, the length of the distance to the ceramic sinking roller. Thick wire diameter zinc dipping time should be long, fine wire diameter zinc dipping time should be short, zinc dipping length is in the range of 2~3.5m, which is also to reduce the zinc consumption of steel wire, is an aspect of maintaining the uniformity of zinc layer.

Materials of qualified quality should be kept marked for reference when used. In order to remove the surface film, surface inclusion and other defects on the surface of the large roll galvanized wire on the surface of the sedimentary layer to the local surface, it can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. The presence of small homogeneous particles of large denier in the tank can stabilize the foam layer, but the accumulation of too many solid particles can cause explosion.