For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by customers. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this thing is more important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized silk, the weight can reach 300kg/ roll or 800kg/ roll.

In the calculation process of 12*14 specifications of barbed rope, it can not be calculated according to the above calculation formula, because first of all, two specifications of raw materials are used, the thinner the wire diameter, the higher the processing cost. Generally speaking, a kilogram of 12*14 barbed rope can reach about 7.5 meters, and the ratio of warp wire to barbed rope cannot be calculated according to the traditional ratio of 7 to 3. The specific use of how much wire and silk need to go through a series of professional measurement but also increase the loss of raw materials and other factors to calculate. Thorn rope factory will also according to customer needs to calculate the reasonable amount of customer use.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, filtration test, and then take a small amount of electroplating solution, with zinc powder treatment after the test, check the problem is solid particles or copper, lead and other foreign metal impurities caused by. One by one, it’s not hard to find the cause of the problem. Galvanized iron wire coating blister, poor adhesion.

If the blade barbed rope produced by the barbed rope factory wants to be made into a straight line, it can’t be made too long because of the constraints of logistics.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging treatment.

If it is not packaged, then a car of blade thorn rope can not be loaded with many pieces, and it is also relatively occupied and easy to lose in the transportation process. The number of the packed blade thorn rope is 50 bundles, and the volume is reduced after hydraulic compression so that it is more convenient to load and unload, and the forklift can easily load and unload. Under normal circumstances, when exporting, the blade thorn rope will be packaged and sold, so that the volume occupied in the container is relatively small, which can be easily placed and will not occupy much place.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.