With a large pickpocket used for steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. The extracted zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the biggest steps to bring zinc consumption down, and it’s a real problem, one that hasn’t been solved for years.

The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.

Galvanized hook mesh standard is thorough, mesh planning: 3cm-20cm, silk planning: 1.2mm-4.5mm, galvanized hook mesh 6000 square meters, some standards are available. Benefits: The selection of low carbon steel wire, surface for cold galvanized (electric galvanized) hot dip galvanized anticorrosion treatment, mesh wire strong, strong protection, long anticorrosion time.

There are many categories of large coils of galvanized wire, and different categories can be applied to different scenarios. Galvanized iron wire common application is the application of the construction industry, one is the use of binding wire, whether it is the binding of scaffolding or reinforcement, need galvanized iron wire to carry out, the common specifications are 22 and 24 wire, common length of 30cm, 35cm, 40cm, 45cm, 50cm. There is also 20kg or 50kg a bundle of 18, 16, 14, 12, 10 galvanized coil wire.

Cold galvanizing (galvanizing) is in the plating tank after the current unidirectional, so that the zinc gradually plated on the metal surface, slow production speed, uniform coating, thin thickness, usually as long as 3-15g, bright appearance, poor corrosion resistance, usually a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower.