In order to remove the photosynovium and oxide remaining on the surface of galvanized iron wire after drawing or heat treatment, it is necessary to do the surface treatment of galvanized steel wire before plating. The common surface of low carbon steel wire is the light synovium or oxide of animal or vegetable oil; Medium and high carbon steel in addition to contain animal or vegetable oil components.

With the increasingly extensive use of hook mesh, the method of bridge rail is also different. The height of sidewalks or seatbelt outer railings should not be lower than 1.10 metres. The net distance between railings should not be greater than 140 mm and horizontal bar rails should not be used. The planning of the hook mesh is necessary to be safe and reliable, the bolt should be installed on the basis of the railing, its strength should meet the requirements of the standard.

There is also in the use of places, blade thorn rope is generally installed and used for the border, walls, prisons and so on, and galvanized thorn rope is in the orchard, fence livestock and so on a large area of installation, although the use of large, but not as high as the use of blade thorn rope and grade, so this is the main reason for the high price. Finally, for the blade barbed wire, the general installation site has high requirements for the protection level, so the quality of the product is also relatively high. But the ordinary galvanized barbed wire has relatively low requirements for the quality in the processing process due to the casual requirements at the installation site.

There is a connection between the hook mesh and the aperture, in short, the general hole small hook mesh, the wire is also very small; Aperture is large, hook mesh wire is generally larger. The weaving of the hook mesh also has certain rules, using the first pre-bent into a wavy wire, and then woven into the hook mesh. According to the knitting method, the hook mesh can be divided into: closed weaving, two-way plain weaving, one-way corrugated weaving, two-way plane weaving, two-way corrugated weaving, rectangular hole weaving.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.

In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.

There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time. However, because the plating solution contains highly toxic cyanide, the gas escaping in the plating process is harmful to the health of workers, and the waste water must be treated strictly before discharge.

With the improvement of people’s living standards, now many families are raising some small pets, these small pets also need a safe nest, pet cage has become an important choice of people, each pet’s habits and living habits will choose to adapt to the cage.

Hot wire mesh in the building wall engineering mainly played the anti-crack effect, inside and outside the use of specifications are not the same. Hot dipped wire material choose low carbon wire, through automation welding precision machinery processing after forming, surface treatment by zinc immersion process, galvanized barbed wire surface smooth and tidy, uniform structure strong, the overall performance is good, even if the local cutting or under pressure will not loose phenomenon occurs, it is the iron mesh strong anticorrosion performance in one of the widely used net class.

The external environment has great influence on the preservation of galvanized wire mesh. In the rainy season, it is necessary to pay attention to the air humidity of the workshop, warehouse and other departments. It is recommended to use a humidifier. Usually, the moisture absorption of book paper is larger than that of powder paper, and the pH value is higher. Generally speaking, in the normal environment of storage wire, storage time of two years is not corroded wire phenomenon. However, it should be noted that in the process of handling the iron wire, it should be handled gently to avoid the position of the coiling coil, which will cause the smooth pulling of the wire and affect the production.

Unless it is a specially customized model, the stainless steel blade barbed rope produced now is generally produced with a 22mm blade length mold, which is what we usually call bto-22 type. It doesn’t have to be the case that there are specifications from 11mm to 65mm. Unless the customer insists on customizing the specified length, the barbed rope manufacturer produces bto-22 stainless steel blade barbed rope.