In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.

In view of this situation, many manufacturers are committed to ensuring the corrosion resistance of titanium and titanium alloy under the premise of increasing the hardness of titanium alloy, and surface carburizing is one of the typical processing technology means. Similar to the surface carburizing treatment of steel, the surface carburizing treatment of titanium alloy is to make the active carbon atoms, diffusion to the internal of titanium alloy, the formation of a certain thickness of higher carbon content of the carburizing layer, after quenching and tempering, so that the surface layer of the workpiece to obtain high carbon content of titanium alloy wire.

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

There are three methods to detect the thickness of zinc layer of galvanized wire: weighing method, cross section microscopy method and magnetic method, among which the first two experiments will cause certain damage to galvanized wire, including the length of galvanized wire and the reduction of dosage. The general detection of galvanized wire galvanized layer is detected by magnetic method, which is also a more intuitive and convenient method. The standard of galvanized layer thickness is related to the wire diameter of galvanized wire. The larger the wire diameter of galvanized wire, the thicker the galvanized layer is. It is the thickness of galvanized layer and cast iron after centrifugal separation.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

Defects such as surface film and surface inclusions can be found and treated by conventional techniques in order to remove them locally from the surface of the deposition layer. Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank.

We must have a certain understanding of the hexagonal net, we are swayed by the beautiful shape of the hexagonal net, not only the shape of the hexagonal net is very beautiful, in fact, the practical value of survival is very high. The introduction of the relevant information should be very clear to know the high-speed road guardrail network, hexagonal mesh of all kinds of guardrail network, the value of the high-speed road is more prominent, it is not only used in a variety of roads, in a variety of sports ball venues and landslides to take care of, but also to reach a very close utility.

The cage door must be open so that the puppy can get out at any time. Once the puppy gets used to the dragon, it will go in without you urging it. Close the door for a few minutes when the puppy is having fun. But keep the crate in a busy area of your home, such as the kitchen. The puppy is relaxed and asleep in the safety of its cage. Cage trained puppies should not be caged for more than two hours during the day (unless you have to, but as soon as you get home from work let the puppy out). After getting used to the crate, the puppy is willing to stay in the playpen. Some dogs can’t stand the small space in a crate, but puppies are less likely to have this problem.