If the zinc coating is good, but in 3% nitric acid when the light, the coating has dark shadow, passivation occurs when the film is brown, may be caused by foreign metal impurities such as copper or lead in the galvanizing liquid. When problems occur in the process of galvanizing large coil galvanized wire, the temperature and current density are checked first, and then the content of zinc and sodium hydroxide in the plating solution is measured and adjusted through the analysis of the plating solution. Whether DPE content is low can be determined by hull cell test.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

When galvanized wire is galvanized, it is generally necessary to pay attention to the following problems: the duration of the protective effect of galvanized wire is greatly related to the thickness of the coating. Generally speaking, in the dry main gas and in indoor use, the thickness of galvanized wire galvanized layer only 6-12 μm “, and in harsh environmental conditions, galvanized wire galvanized layer thickness needs 20μm “to B height up to 50μm”. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire.

In order to improve the corrosion resistance of steel pipe, the general steel pipe is galvanized. Galvanized steel pipe is divided into hot dip galvanized and electric galvanized. The layer of hot dip galvanized is thick, the cost of electric galvanized is low, and the surface is not very smooth. Used for steel blowing oxygen pipe, generally with small diameter welded steel pipe, specifications from 3/8-2 inches of eight. Made of 08, 10, 15, 20 or 195-Q235 steel strip, in order to prevent corrosion, some should be aluminized.

Hexagonal net structure can be used for slope support, excavation, rock face net mine support form, slope vegetation (green color), railway road isolation block, it can be made into a cage, cushion, used for rivers, flood dam and seawall erosion protection and storage reservoir, river closed cage. Driving and guiding rivers, river flood disaster is a major water and river erosion of destruction, resulting in flooding, resulting in a great deal of loss of property by the amount of soil and water dissipation. Because of this, in dealing with these problems, the application of the habitat grid structure becomes a solution plan, which has the potential to protect the bank forever.

Different from the general zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach the former 6-8 times, so in the service life also has a great advantage, ordinary products three or five years began to corrosion and the latter will take longer to change. Stainless steel barbed rope is in the material aspect of protection, so the durability is also better, these two products are long in the service life, but in the price is high.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

At present, there are two processing methods of blade stabbing rope. One is to make it into a spiral shape, and then make a clip treatment. It is not only our common spiral blade stabbing rope, but also a single spiral blade stabbing rope without clip, but even a single helix can not stretch it to a relatively straight. This is mainly because the blade barbed rope is wrapped and wound at the same time, so it can only be spiral.