Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

Hot dip galvanized hexagonal net is made of low carbon steel wire by mechanized braided welding and then by hot dip zinc treatment. The net color is white and shiny, thick zinc layer, uniform mesh, flat mesh surface, solder joint tension resistance, high corrosion resistance. The surface of the steel wire is usually protected by hot-dip galvanizing, and the thickness of the galvanized protective layer can be made according to the requirements of customers. Hot-dip galvanizing hexagonal net is another kind of twisting mesh corresponding to the galvanizing hexagonal net.

3. Acid activation acid activation solution should be able to remove corrosion products and oxide film (skin) on the surface of parts, without excessive corrosion on the matrix.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

The surface coating of galvanized wire can be seen whether the quality of galvanized wire is good or not. If the strength of zinc attached to the wire is very poor, then this galvanized wire do not buy, because this galvanized wire must be poor galvanized wire. High quality galvanized wire in general, the zinc layer attached to the surface of the wire is relatively thick, so when we buy galvanized wire, as long as we look at the thickness of the zinc layer, we can generally judge the quality of galvanized wire.

Some customers do not understand the range of application of different styles of barbed rope, so there is a big difference.