The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

Immersed six edge barbed wire corrosion lost the original characteristics, in the shape, color and mechanical properties and other aspects will change, resulting in equipment damage, pipeline leakage, specifically, is prone to fracture, lose the original protection function. Corrosion usually metal corrosion has three types: physical, chemical corrosion and electrochemical corrosion, and corrosion depends on the chemistry of the metal itself and the organizational structure, still have relationship with the surrounding medium, such as wet environment than dry environment is easy to rust, more less than the impurities of impurities is easy corrosion, high temperature conditions than under the condition of low temperature corrosion, etc. After understanding these, we can effectively prevent the corrosion of the six sides of the wire, prolong the service life of the product.

Each coil of steel wire shall consist of one wire. The surface of the rod shall not have cracks, folds, scars, ears, layers or inclusions. However, indentation, pits, bumps, scratches and pockmarks are allowed, and the depth or height shall not be 0.2mm. There should be no corrosion and oxidation skin on the surface of the steel wire, and oxidation color is allowed by heat treatment. The surface of the wire is allowed to have scratches not exceeding half of the allowable deviation range of the diameter, and local defects not exceeding the allowable deviation of the appropriate diameter.

The production process of stainless steel blade barbed wire is basically similar to that of galvanized blade barbed wire, and the blade size is usually determined according to the mold.

Galvanized iron wire can be divided into hot-dip galvanized iron wire and cold galvanized iron wire according to different processing methods. Galvanized iron wire is more prominent in its corrosion resistance. Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Galvanized iron wire products are widely used in construction, handicrafts, wire mesh preparation, the production of galvanized hook mesh, wall mesh, highway guardrail, product packaging and daily civilian and other fields.