Because zinc layer corrosion resistance, can be applied to all kinds of environment, use is also very convenient, has been more popular hardware products. Galvanized iron wire should pay special attention to the acyl washing, to slowly put into the container, to prevent acid sputtering on the body, and prohibit the water into the water, so that it is easy to let the acid out, to learn to handle gently, stacking should also be firm and neat. It can be widely used in architecture, handicrafts and other daily civilian applications.

1, galvanized wire mesh molding sheet must be packed with flat hard data, to avoid eternal deformation due to poor packaging.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

Some customers do not understand the scope of application of different styles of barbed rope, there is a great difference.

Since galvanized iron wire will rust, we need to pay attention in the process of storage and use, try to store in a dry and ventilated environment, in the process of use to avoid damaging the surface of galvanized iron wire, we can slow down the time of galvanized iron wire rust.

Electric galvanized shaft wire direct selling is in the plating tank through the current unidirectional zinc gradually plated on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanizing shiny white.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.