Welding mesh is also known as external wall insulation wire mesh, galvanized wire mesh, galvanized welding mesh, wire mesh, row welding mesh, touch welding mesh, construction mesh, external wall insulation mesh, decorative mesh, barbed wire, square eye mesh, screen mesh, anti-crack mesh. Stainless steel welding net, is made of high quality stainless steel wire row welding, more acid resistance, alkali resistance, solid welding, beautiful, wide use and so on.

Bridge protection system generally do not need to be specially installed special drainage system, the use of hexagonal mesh made of gabion mesh box, the inside of the filler are selected stones, these stones are not easy to wear, and between the stones and stones will retain some gaps, so it is very good to meet the drainage requirements.

The barbed wire factory will store the blade barbed wire inventory in the appropriate place, because it understands the product characteristics.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.

This process has no mold, low processing cost, easy forming, can process a variety of shapes and other characteristics are widely used. But the products of the guardrail are powder impregnated plastic. According to whether it needs heating, it is divided into hot dipping and cold dipping. According to the raw materials of dipping, it can be divided into liquid dipping and powder dipping. Hot-dip galvanizing, as a metal anticorrosion method, is usually to put the steel structure to be derusted into the zinc liquid at about 500℃, so that the zinc layer is attached to the surface of the steel structure.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.