Hot-dip galvanized wire has longer service life and better corrosion resistance than ordinary steel wire. Hot dip galvanizing is a method of chemical combination of zinc metal and steel wire surface, through the formation of a strong and self-healing zinc-iron alloy protective layer on the steel wire surface, so as to prevent direct contact between the steel wire and the external environment, reduce the possibility of oxidation corrosion, and extend the service life of the steel wire.
The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.
Spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and resistance to impact and oscillation. The strength and endurance objectives, especially to prevent the occurrence of modification cracks, are the key to the consumption of spring wire. The inner quality and outer quality of the wire rod directly affect the function of the wire.
Cold plating is a physical treatment method, the zinc is simple and uneven, the amount of zinc is also less than in the corrosion and rust prevention and chemical disposal of hot plating; The amount of hot zinc plating is relatively thick, the surface of the disposal is flat on average, and it is not easy to fall off. A layer of alloy composed of zinc and metal has very strong oxidation ability, and there is a layer of pure zinc on the outside of this layer of alloy, which is why hot plating is thicker and stronger than cold plating. Under the condition of high degree of natural recovery, galvanized hook net can play a very good maintenance effect on the environment, it is not afraid of wind and rain, it is the battle machine in the hook net, much stronger than the dip plastic hook net.
The use of galvanized anticorrosion treatment is better, the metallurgical connection between galvanized layer and steel, combined with the appearance of steel as a whole, making the coating more durable, more reliable. In the suburbs, the galvanized thickness of hot dip galvanized can adhere to more than 50 years without repair, in the suburbs or near the seaside, galvanized layer can adhere to more than 20 years without repair, is the choice of anti-rust and anti-corrosion. Coating has strong toughness, in the process of transportation or use, can resist extrusion, withstand some damage, hot dip galvanized anticorrosion treatment both save time and effort, and faster than other processing, than dipping, spraying to save much time and effort.
The utility of the hexagonal net in the playground is very superficial, in each city to build the playground, are less than the shadow of the hexagonal net. In the stadium around the installation of hexagonal nets, not only can improve the stadium group image, but also convenient city residents to carry out a row of activities.
In order to improve the corrosion resistance of steel pipe, the general steel pipe is galvanized. Galvanized steel pipe is divided into hot dip galvanized and electric galvanized. The layer of hot dip galvanized is thick, the cost of electric galvanized is low, and the surface is not very smooth. Used for steel blowing oxygen pipe, generally with small diameter welded steel pipe, specifications from 3/8-2 inches of eight. Made of 08, 10, 15, 20 or 195-Q235 steel strip, in order to prevent corrosion, some should be aluminized.
The wire rod should be normalized or soxhlet processed, instead of spheroidal annealing for standard large ones. Soxhlet process is widely used in the heat treatment of the center, especially the products before drawing. Avoid decarbonization during heat treatment. After heat treatment, sulfuric acid or hydrochloric acid pickling is used to remove iron sheet. The coating (see smooth carrier) can be dip-lime, phosphating, borax treatment or copper plating.
If not packaged, then a car of blade thorn rope can not be loaded with many pieces, but also relatively occupied places and easy to be lost in the process of transportation. Each bundle of blade barbed rope is 50 bundles. After hydraulic compression, the volume is reduced and it is more convenient to load and unload. Forklift trucks can load and unload easily. In general, when exporting, the blade thorn rope will be packaged for sale, so that the volume occupied in the container is relatively small, which can be very easy to size and place will not take up much place.
3, a wide variety of specifications, a variety of shapes you choose, both European and American style and today’s popular fashion, full noble and modern beauty.
In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.
4, galvanized can be used zincate galvanized or chloride galvanized process, should use appropriate additives to meet the requirements of this standard coating.
According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:
Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging.