If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.

With the technique of preventing the coating from peeling off the hook mesh, hook tennis court chain link fence systems have long tended to define lines that economically attach amenities and add value to the property. The interlocking system also allows deductions for easy attachment control.

In order to orchard special electric galvanized shaft wire in alluvial surface to partially remove the surface film layer, surface impurity and other shortcomings can be found and solved according to the basic technology; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. The large amount of fine homogeneous particles in the tank can stabilize the foam layer, but the accumulation of too much solid particles will cause explosion.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Stainless steel blade barbed rope production process is basically similar to galvanized blade barbed rope production process, usually according to the mold to determine the size of the blade.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

Razor blade barbed rope has been widely used in military sites, prisons, government agencies, banks in the world. The walls of living quarters, private homes, villas, fences, doors and Windows, highways, railway guardrail and border lines and other protection and security.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

The main difference is carbon content. Iron has a carbon content of 2.11 percent or more, while steel has a carbon content of 2.11 percent or less. Iron-carbon alloys with carbon content of more than 2.11% are cast iron (pig iron), which are basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different, and the content of harmful impurities such as sulfur and phosphorus in steel is smaller. Wire general color key, wire color light point, white point.

The characteristics of large volume galvanized wire is smooth and bright surface, but wet will affect the brightness of galvanized wire, so we must pay attention to avoid humidity when storing, can support a shelf on the ground, so that galvanized wire and the ground isolation, so that it will not be affected by the surface moisture, there is to pay attention to the change of weather, to avoid galvanized wire rain. Galvanized wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance.