6, according to the wire diameter thickness to adjust zinc dipping time. Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is the length of the distance between the lead screw on the zinc pot and the ceramic sinking roll. The zinc dipping time of coarse wire diameter should be long, and the zinc dipping time of fine wire diameter should be short.

Poor pretreatment before electroplating; Bath temperature is too low; Poor quality additives or excessive additives and organic impurities can cause poor bonding. The quality of the additive also has an effect on coating foaming. Some additives react incompletely during synthesis and continue to polymerize during long-term storage or use. The additive tends to distort the lattice and create stress, causing the coating to blister.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging.

There is also a straight blade stabbing rope, which is mainly because the board and wire are not wound in the process of wrapping, so the blade stabbing rope produced is a straight product. The length of the barbed rope of this specification cannot be too long due to the limitation of logistics, and it cannot be bent because it is easy to be deformed by force. This is also the main reason why the barbed rope of the straight blade is not whole or long. Customers are advised to determine the spacing before purchase to prevent losses caused by no calculation.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

The blade gill net has 3-7 buckles every 2 turns, and it is a circle card. After being opened, it forms a spiral shape. When stretching, you must take protective gloves to prevent scratches. When opening, only one side of the gill net needs to be fixed, and then the gill net needs to be opened in the opposite direction. Pay attention to the spacing of the holes should not be too large, otherwise it will affect the aesthetic effect. As long as the time to slowly return to the line, simple operation, convenient construction.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.

The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate. The concentration of plating aid should not be too high. Hot plating wire must be added ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution is controlled in the range of 50~80g/L. The addition of ammonium chloride or zinc chloride raw materials without the results of laboratory analysis shall be subject to criticism and education, and economic treatment if necessary.

Cold galvanized by electrolytic action to metal and other materials surface attached to a layer of metal film, so that the surface of the material uniform texture, anti-corrosion wear, appearance is more beautiful. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other “rough” workpiece long-term rust prevention.

Annealed wire is mainly made of soft iron wire through low carbon steel heating, hot drawing, constant temperature and other processes. Because of the differences in use, there are also different in the production process, and the specifications are varied. Annealed wire can be widely used, mainly because annealed wire and other kinds of wire, has many advantages.

The distance between the adjacent two thorn rope installation do not know whether you have noticed? Careful observation can find that its spacing is not the same, the thorn rope factory for customer consultation when asking the installation height of the reason.