At present, there are two processing methods of blade stabbing rope. One is to make it into a spiral shape, and then make a clip treatment. It is not only our common spiral blade stabbing rope, but also a single spiral blade stabbing rope without clip, but even a single helix can not stretch it to a relatively straight. This is mainly because the blade barbed rope is wrapped and wound at the same time, so it can only be spiral.

What’s the difference between cold galvanized wire and hot galvanized wire? It is mainly different production process. Cold galvanized iron wire, also known as electric galvanized iron wire, is the use of electrolytic galvanizing process, and hot galvanized iron wire is the use of hot penetration galvanizing process. Compared with the two, hot dip galvanized iron wire thick coating, high zinc content, has stronger anti-corrosion and anti-rust effect. Similarly, the price is also higher, cold galvanized iron wire and hot galvanized iron wire which good? Mainly for the use of scenarios and requirements to choose appropriate galvanized iron wire, appropriate is better.

Bridge protection system generally do not need to be specially installed special drainage system, the use of hexagonal mesh made of gabion mesh boxes, the inside of the filler are selected stones, these stones are not easy to wear, and between the stones and stones will retain some gaps, so it is very good to meet the drainage requirements.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

With a large pickpocket used for steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. The extracted zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the biggest steps to bring zinc consumption down, and it’s a real problem, one that hasn’t been solved for years.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the amount of surface-active substances brought in to Z. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.