Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

As we all know, the mechanism of resistance to atmospheric corrosion of zinc includes mechanical protection and electrochemical protection. Under the condition of atmospheric corrosion, there are ZnO, Zn(OH)2 and basic zinc carbonate protective film on the surface of zinc layer, which to a certain extent slows the corrosion of zinc. When this protective film (also known as white rust) is damaged, a new film will be formed.

Construction welding net work wall insulation project using galvanized welding network in wall insulation and rust engineering project plays a necessary role, wall painting batch putty network is divided into two kinds: this is galvanized welding network; Another is to change the wire drawing wire welding mesh, according to the provisions of the region, construction enterprises to carry out effective material selection. Construction welded wire mesh new mink cage new mink cage grommet see more 1 inch, from silk in 2 mm up and down, management method is simple and easy, a mesh surface bright and clean and is not easy to scratch mink, galvanized welded wire online zinc quantity proportion, it is not easy to rust, new mink cage up more convenient, mink settled in natural environment more comfortable, the price also is higher than before the same specifications of the mink cage competitive many, But the overall character is not harmed at all, it is stronger.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.