The production process of large coil galvanized wire is relatively simple. The wire after cleaning is put into electroplating solution first. Of course, the plating solution should contain zinc oxide, a direct current of steel, another zinc plate in the plating solution. The zinc is transferred to the surface of the steel as a molecule. If it shows a bright and beautiful color, the wire is coated with zinc.

In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.

In order to make the zinc content of steel wire stable in the future, and maintain its uniformity, as far as possible to reduce the zinc content, and effectively reduce zinc consumption to the actual work, the following measures are proposed by the wire factory:

Friends in the industry know that galvanized iron wire has two kinds of cold galvanized iron wire and hot galvanized iron wire, so what is the difference between cold galvanized iron wire and hot galvanized iron wire? Which is good?

Thorn rope factory production per ton of product profit is not particularly high so in the sales price to wholesale, many users always think that thorn rope price has a lot of profit space so they are eager to lower the price, some manufacturers in order to sell out on the use of low price promise and then underweight behavior. Often the actual user spends less money with the lack of weight is almost the same, so the unit price is relatively high. Because the quotations of the thorn rope factory are in accordance with the real price, the quality is guaranteed. In this way, the customers will not look for debts after the purchase, and the subsequent purchase work will still find us, so that we can benefit.

Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.