What’s the difference between cold galvanized wire and hot galvanized wire? It is mainly different production process. Cold galvanized iron wire, also known as electric galvanized iron wire, is the use of electrolytic galvanizing process, and hot galvanized iron wire is the use of hot penetration galvanizing process. Compared with the two, hot dip galvanized iron wire thick coating, high zinc content, has stronger anti-corrosion and anti-rust effect. Similarly, the price is also higher, cold galvanized iron wire and hot galvanized iron wire which good? Mainly for the use of scenarios and requirements to choose appropriate galvanized iron wire, appropriate is better.

Titanium alloy with low carbon content is obtained because the carbon content remains the original concentration. The hardness of titanium alloy is mainly related to its carbon content. Therefore, after carburizing and subsequent heat treatment, the workpiece can obtain the performance of hard and tough inside. Galvanized wire varieties are mainly classified into three categories: electric galvanized wire, hot galvanized wire and galvanized wire. Among them, the classification of galvanized wire is divided into large roll galvanized wire, medium roll galvanized wire, small roll galvanized wire, galvanized shaft wire, truncated galvanized wire and other main production varieties.

If the blade barbed rope produced by the barbed rope factory wants to be made into a straight line, it can’t be made too long because of the constraints of logistics.

Some customers do not understand the scope of application of different styles of barbed rope, there is a great difference.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

We basically know that the barbed wire fence generally has two kinds of ring and linear filamentous, the overall protective wire mesh selection of galvanized, stainless steel processing raw materials, long-term use is not easy to rust. Barbed wire fence uses stainless steel barbed wire, plastic coated barbed wire, aluminum coated barbed wire, galvanized barbed wire and other raw materials through special wire drawing into the strand planning, has a strong role in protection and maintenance. Widely used on both sides of the highway, grassland, gardens and other places, because it is a field protection product and therefore updated faster, so how to use the barbed wire fence after abandonment? Here are some of the uses of discarded blades.

Its wire diameter specifications include: 8#-24#, with thick coating, corrosion resistance, strong coating and so on. And according to the special needs of users, according to industry standards to provide various specifications of galvanized wire. Low carbon steel wire is called galvanized iron wire after drawing and galvanized, so galvanized wire products have certain characteristics. In order to better let galvanized wire play an effect, in the process of galvanized wire, generally according to customer needs to control the thickness of galvanized wire zinc layer, so that galvanized wire can meet the needs of customers.

Fence use: The use of the fence is generally one meter two to two meters a height of the impregnated welding mesh, mesh mostly 6cm, wire diameter from 2mm to 3mm.

There are many categories of large rolls of galvanized wire, and different categories can be applied to different scenarios. The common application of galvanized iron wire is the application of the construction industry. One is the use of binding wire. Whether it is the binding of scaffolding or reinforcement, galvanized iron wire is needed to carry out. There are also 20kg or 50kg bundles of No. 18, No. 16, No. 14, No. 12, No. 10 galvanized coils.

Poor pretreatment before plating; Bath temperature is too low; Poor quality of additives or too many additives and organic impurities will cause poor bonding. The quality of additives also has an effect on coating foaming. Some additives react incompletely during synthesis and continue to polymerize during long-term storage or use. The additive tends to distort the crystal lattice and cause stress, causing the coating to bubble.