Galvanized iron wire is a substance we often see in life. It is the zinc gradually plated on the metal surface through the unidirectional current in the electroplating tank. The production speed is slow, the coating is uniform, the thickness is thin, usually only 3-15 microns, the appearance is bright, the corrosion resistance is poor, and the corrosion will rust in a few months. Galvanized wire has the characteristics of thick galvanized layer, strong corrosion resistance, strong galvanized layer, etc., the products are widely used in construction, highway walls, Zahua, weaving nets.

Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.

Many pet cages are designed with a small box in the base, so that pets can clean up when they poop, but also convenient for pets’ health. For example, if there is no excreta box, pet excreta will be on the ground, which is quite unhealthy. If you have a box, it’s easy to take the box out and wash the trash away so it doesn’t get all over the place, so it’s more hygienic.

Now it is mainly 12 or 14 galvanized barbed rope. Although they are calculated according to the price per ton, the calculation is different when it comes to every meter, because the thickness of the silk is not the same, which causes the problem that one galvanized barbed rope of equal weight is longer and the other is longer. Customers must have detailed communication with the barbed rope factory before purchasing to avoid such problems.

Spray powder mainly acrylic powder, polyester powder and so on. Dipping is a kind of plastic coating process, that is, the plastic coating on the matrix, generally metal, such as: daily use of clothes hangers, pliers handles, scissors on the rubber sleeve, various handrails, etc. Plastic immersion is to heat the metal to spray plastic powder evenly on the metal to form a plastic film, or heat immersion liquid into the metal to cool it and then plastic coating on the metal surface.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.

Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.