Hot drawing is the heating before the wire enters the die hole, mainly used for high melting point wire drawing; The temperature drawing is carried out by heating the heater to the range of temperature, mainly used for galvanized steel wire, difficult to deform drawing.

The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.

Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.