After annealing, the extension rate of galvanized wire is increased, making the product more soft and increasing the scope of application of galvanized wire. After electric galvanized hot galvanized, electroplated copper and other widely used screen production. Building reinforcement binding with galvanized wire mesh braided with the first after plating, plating and other methods, after treatment of galvanized wire mesh or steel wire mesh, has good corrosion resistance, oxidation resistance characteristics, can be used in construction, petroleum, chemical, aquaculture, garden protection, food processing and other industries reinforcement, protection and heat preservation.

Stainless steel blade barbed wire production process is similar to galvanized blade barbed wire production process, usually according to the mold to determine the size of the blade.

The cooling circulation system uses spray to cool the drawing die, and takes away a lot of heat generated by the drawing machine in high speed drawing in time to ensure the quality of the wire. Control drawing process parameters: drawing speed 10 ~ 12m/s; Winding tension 8 ~ 10N; Measuring length 30km; The mass fraction of lubricant is 3.5 ~ 4.5%; pH value of lubricant 7 ~ 8; Lubricant temperature 30 ~ 40℃.

The impregnated hexagonal wire mesh will lose its original characteristics after corrosion, and will change in shape, color and mechanical properties, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment than dry environment easy corrosion, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated hexagonal wire mesh, prolong the service life of products.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.