There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time. However, because the plating solution contains highly toxic cyanide, the gas escaping in the plating process is harmful to the health of workers, and the waste water must be treated strictly before discharge.

Pet cage is generally made of high quality iron wire, low carbon steel wire, stainless steel wire welding, which is characterized by beautiful, lightweight, folding, easy to store. The surface treatment of pet cage is generally: cold galvanized, hot galvanized, spray, dip, chromium plating, nickel plating and other methods.

Pet cage is generally made of high quality iron wire, low carbon steel wire, stainless steel wire welding, its characteristics are beautiful, light, folding, easy to store. Pet cage surface treatment is generally: cold galvanizing, hot galvanizing, spraying, dipping, chrome plating, nickel plating and other methods. Pet cage is mainly used for family breeding pets and protection.

The size of the galvanized layer of galvanized iron wire is related to the anti-corrosion ability and application effect of galvanized wire. The thickness of the galvanized layer of the general standard galvanized wire products should be tested after the product is formed. There are three specific test methods. Weighing method and cross section microscopy method are destructive experimental methods, and magnetic method is a relatively rigorous non-destructive method, but the measurement steps and requirements are relatively high, so they are rarely used in specific applications. The first two methods are intuitive and common methods.

Poor pretreatment before plating; Bath temperature is too low; Poor quality of additives or too many additives and organic impurities will cause poor bonding. The quality of additives also has an effect on coating foaming. Some additives react incompletely during synthesis and continue to polymerize during long-term storage or use. The additive tends to distort the crystal lattice and cause stress, causing the coating to bubble.

The insulation layer of large rolls of galvanized wire and rigid thermal insulation products can be bound with double strands of galvanized iron wire, and the binding interval shall not exceed 400mm. The pipe or corresponding equipment with nominal diameter equal to or greater than 600mm shall stop reinforcement after binding, and the enclosed galvanized steel wire must be winched. The iron or wood rod should be tightened, but the tightening level should be moderate, not too tight or too loose, and not damage the wire. The consumption of wire and steel wire is generally used in drawing process and galvanized disposal.

Large rolls of galvanized wire in oxygen violently extinguished, spark, and sodium block, magnesium strip in oxygen extinguished, no spark phenomenon. This phenomenon is determined by the composition of galvanized wire. The galvanized wire used in the experiment is pig iron or steel wire, pig iron and steel are iron and carbon alloy, containing iron and carbon two elements of complex material. Carbon in galvanized wire will produce carbon dioxide when extinguished, solid into gas, volume will shrink rapidly.